PRO MASTER Multilayer Zirconia Block for 89mm Amann Girrbach System
| Color | A1,A2,A3,A3.5,A4,B1,B2,B3,B4,C1,C2,C3,C4,D2,D3,D4,OM1,OM2,OM3 |
| Flexural Strength | 800-1300MPa(Av.) |
| Material Adaptation System | 92x75mm |
| Sintered Density | 6.07±0.03 g/cm³ |
| Sintering Temperature | 1500 °C |
| Thickness | 10mm, 12mm, 14mm, 16mm, 18mm 20mm, 22mm, 25mm |
| Translucency | 57%-43% |
| Vickers Hardness (HV10) | 1200 HV |
- Product Code: PRO-MASTER-Multilayer-Zirconia-89mm-Amann-Girrbach
- Availability: In Stock
-
$175.00
Available Options
This PRO MASTER Multilayer Zirconia Block is engineered specifically for the 89mm Amann Girrbach milling system. The 89mm disc format fits directly into Amann Girrbach holders without adapters, and its multilayer gradient delivers seamless color transitions from cervical to incisal for lifelike anterior restorations. Each block undergoes CIP (Cold Isostatic Pressing) at 200 MPa for uniform density, eliminating internal voids that cause chipping during high-speed AG milling cycles.
Pro Master Zirconia exhibits a natural, four-dimensional gradient of color, clarity, strength, and hardness, making it your laboratory's top choice. Pro Master Zirconia improves the quality of all-ceramic dentures while remaining resistant to deformation and offering enhanced toughness. Transparency decreases from the incisal edge to the cervical region (57%-43%), while hardness and strength increase from the incisal edge to the cervical region (800-1300 MPa). Available in 16 classic shades and three bleached shades, it's suitable for all dental indications.
For professional dental laboratory use only.
| Specifications | |
| Color | A1,A2,A3,A3.5,A4,B1,B2,B3,B4,C1,C2,C3,C4,D2,D3,D4,OM1,OM2,OM3 |
| Flexural Strength | 800-1300MPa(Av.) |
| Material Adaptation System | 92x75mm |
| Sintered Density | 6.07±0.03 g/cm³ |
| Sintering Temperature | 1500 °C |
| Thickness | 10mm, 12mm, 14mm, 16mm, 18mm 20mm, 22mm, 25mm |
| Translucency | 57%-43% |
| Vickers Hardness (HV10) | 1200 HV |