4D PRO Multilayer Zirconia Block for 89mm Amann Girrbach System
| Color | A1,A2,A3,A3.5,A4,B1,B2,B3,B4,C1,C2,C3,C4,D2,D3,D4,OM1,OM2,OM3 |
| Flexural Strength | 700-1200MPa(Av.) |
| Material Adaptation System | 92x75mm |
| Sintered Density | 6.07±0.03 g/cm³ |
| Sintering Temperature | 1500 °C |
| Thickness | 10mm, 12mm, 14mm, 16mm, 18mm 20mm, 22mm, 25mm |
| Translucency | 57%-43% |
| Vickers Hardness (HV10) | 1200 HV |
- Product Code: 4D-Pro-Multilayer-Zirconia-89mm-Amann-Girrbach
- Availability: In Stock
-
$87.50
Available Options
Ultra-High Translucency 8-Layer Gradient Zirconia for Premium Aesthetics
4D PRO Multilayer Zirconia Block for 89mm Amann Girrbach Ceramill Systems
The 4D PRO Multilayer Zirconia Block represents the next generation of dental zirconia technology, specifically designed for the 89mm Amann Girrbach Ceramill milling platform. With an advanced 8-layer gradient structure and ultra-high translucency, the 4D PRO delivers unparalleled aesthetic results that rival the natural beauty of human dentition.
Next-Generation Translucency
The 4D PRO features an upgraded material composition achieving translucency up to 60% while maintaining exceptional flexural strength of 800-1150 MPa. The proprietary 8-layer gradient technology creates ultra-smooth transitions in color, opacity, and fluorescence from the cervical base to the translucent incisal edge, producing restorations that are virtually indistinguishable from natural teeth.
Premium Shade Selection
- 16 VITA Classic Shades — complete A1-D4 shade coverage
- 11 Natural Shades — organic color reproduction
- 3 Bleached Shades — for bright, white aesthetics
- Custom Shades — available on request for large orders
Clinical Applications
- Premium anterior crowns and veneers
- High-aesthetic posterior crowns
- Multi-unit bridges (up to 14 units)
- Implant-supported restorations
- Full-arch rehabilitations
- Inlays and onlays
Technical Specifications
| Parameter | Value |
| Material | Yttria-Stabilized Zirconia (4Y-TZP / 5Y-TZP) |
| Flexural Strength | 800-1150 MPa |
| Translucency | Up to 60% |
| Gradient Layers | 8 Layers |
| Disc Diameter | 89mm (Amann Girrbach) |
| Thickness Range | 10-25mm |
| Sintering Temp | 1450°C - 1550°C |
| Compatible Machines | Ceramill Matik, Matron, Motion 3 |
4D PRO vs 3D Plus: Which Should You Choose?
| Feature | 4D PRO | 3D Plus |
| Translucency | Up to 60% | 43-57% |
| Layers | 8 | 6 |
| Best For | Premium aesthetics | All-round use |
Frequently Asked Questions
What makes the 4D PRO different from the 3D Plus?
The 4D PRO offers superior translucency (up to 60% vs 43-57%), more gradient layers (8 vs 6), and higher strength (800-1150 MPa vs 700-1050 MPa). It is the premium choice for cases requiring the highest level of aesthetics.
Can I use the same sintering protocol as the 3D Plus?
The sintering temperature range is similar (1450-1550°C), but we recommend following the specific sintering curve provided with the 4D PRO for optimal results. Speed sintering protocols are also available.
Is the 4D PRO suitable for long-span bridges?
Yes, with a flexural strength of 800-1150 MPa, the 4D PRO is suitable for multi-unit bridges up to 14 units. Its high strength ensures reliable long-term performance even for demanding prosthetic cases.
For professional dental laboratory use only.
| Specifications | |
| Color | A1,A2,A3,A3.5,A4,B1,B2,B3,B4,C1,C2,C3,C4,D2,D3,D4,OM1,OM2,OM3 |
| Flexural Strength | 700-1200MPa(Av.) |
| Material Adaptation System | 92x75mm |
| Sintered Density | 6.07±0.03 g/cm³ |
| Sintering Temperature | 1500 °C |
| Thickness | 10mm, 12mm, 14mm, 16mm, 18mm 20mm, 22mm, 25mm |
| Translucency | 57%-43% |
| Vickers Hardness (HV10) | 1200 HV |